Product Description
NM400 NM500 wear resistant steel plate wear plates
Abrasion Resisant Plate AR400 AR500
Abrasive resistant steel
Hard steel plate
hard 500 hard 400
steel plate cutting and bending
1.Production Process
1)Steelmaking process Flow Chart
Blast Furance+Hot Metal Ladle Truck+KR Hot Metal Treatment+Converter+LF Refining Furnace+RH Vacuum Degassing Furance+Con-cast
2.Rolling Process Flow Chart
Reheating Furance+High-pressure Water Descaling+Edger Mill+Roughing Mill+Finishing Mill+Accelerated cooling+Hot Leveler+Marking and Spray Printing+Cooling Bed+On-line UT+Crop Shear+Double-side Trimming Shear+Cut-to-length Shear+Measurement+Marking and Spray Printing+Cold Leveler/Heat treatment
3.Heat-Treatment Flow Chart
Plate+Shot Blasting+Quenching Furance+Quenching Machine+Tempering Furance+Warm Leveler+Cooling Bed+Cutting+Cold Leveler+Finishing&Packaging
4.Thickness and Width
Thickness:4.5mm-150mm
Width:1600mm-4100mm
5.Main Grade
Germany:XAR400,XAR450,XAR500,XAR600,Dillidur400,Dillidur500
Belgium:QUARD400,QUARD450,QUARD500
France:FORA400,FORA500,Creusabro4800,Creusabro8000
Baosteel:B-HARD360,B-HARD400,B-HARD450,B-HARD500
HBIS:NM360,NM400,NM450,NM500
Finland:RAEX400,RAEX450,RAEX500
Japan:JFE-EH360,JFE-EH400,JFE-EH500,WEL-HARD400,WEL-HARD500
6.Chemical Composition&Property
| Grade | c | Si | Mn | P | S | Al | Cr+Ni+Mo | Nb+V+Ti |
| NM400 | 0.10-0.40 | 0.20-0.40 | 1.00-2.00 | Max 0.015 | Max 0.003 | Min 0.020 | Max 0.9 | Trace Amount |
| NM450 | 0.10-0.40 | 0.20-0.40 | 1.00-2.00 | Max 0.015 | Max 0.003 | Min 0.020 | Max 1.2 | |
| NM500 | 0.10-0.40 | 0.20-0.45 | 1.00-2.00 | Max 0.015 | Max 0.003 | Min 0.020 | Max 1.5 | |
| NM550 | 0.10-0.50 | 0.20-0.45 | 1.00-1.50 | Max 0.015 | Max 0.003 | Min 0.020 | Max 2.0 | |
| NM600 | 0.10-0.50 | 0.20-0.45 | 1.00-1.50 | Max 0.015 | Max 0.003 | Min 0.020 | Max 2.5 | |
| XCHD400 | 0.10-0.30 | 0.20-0.40 | 1.00-2.00 | Max 0.015 | Max 0.003 | Min 0.020 | Max 0.1 | |
| XCHD450 | 0.10-0.40 | 0.20-0.40 | 1.00-2.00 | Max 0.015 | Max 0.003 | Min 0.020 | Max 0.9 | |
| XCHD500 | 0.10-0.40 | 0.20-0.45 | 1.00-2.00 | Max 0.015 | Max 0.003 | Min 0.020 | Max 1.5 |
7.
| Grade | Size(mm) | RP0.2(Mpa) | Rm(Mpa) | A50(%) | AKV,(ºC) | KV2(J) | HBW | ||
| NM400 | 100 | 1233 | 1337 | 15 | -20 | 35 | 37 | 42 | 415 |
| NM450 | 60 | 1345 | 1434 | 9.5 | -20 | 72 | 59 | 58 | 455 |
| NM500 | 50 | 1608 | 1706 | 10.5 | -20 | 43 | 50 | 45 | 495 |
| XCHD400 | 35 | 1025 | 1161 | 17.5 | -40 | 52 | 45 | 40 | 413 |
| XCHD450 | 30 | 1281 | 1400 | 10.5 | -40 | 45 | 48 | 52 | 453 |
| XCH500 | 6 | 1465 | 1529 | 13.5 | -40 | 24 | 24 | 22 | 515 |
Product Display
1) Manufacturing Technique
Cutting large steel plates as your requirements to make the surface of the plate bright by miling and grinding, also can make holes and make angle degrees,and can weld by your drawing.
For the thickness under 30mm, cutting by laser; For thickness over 30mm, mainly OXY-cut, flame cutting.
For the thickness 200mm steel plate, because during the flame cutting, the temperature is very high, so the cutting parts steel plate might be broken at the angle part, then our workers will repair the angles to be good condition.
2) Application
Wear-resistant steel plate with high wear resistance and good impact performance is good, can be cutting, bending, welding, etc., can adopt welding, plug welding, bolt connection way to connect with other structures, such as the scene of the maintenance process possesses the characteristics of time saving, convenient and widely used in metallurgy, coal, cement, power station, glass, mining, building materials, brick and petrochemical industry, compared with other materials, has a high cost performance, has been favored by more and more buyers.
Hot Tags: nm500 wear resistant steel plate ar500, China, manufacturers, suppliers, factory, MN13 Grade Manganese Plate, MN13 Grade Manganese Plate, X120Mn12 High Manganese Steel Plate, AISI 4140 Steel Sheet, 1 3401 High Manganese Steel Plate