Sichuan Liaofu Special Steel Company is one of the most experienced manufacturers and suppliers of wholesale 18crnimo7-6 din 1.6587 forged steel round rod in China. With over 20 years' experience, our factory offer high quality products made in China with competitive price. Welcome to contact us for wholesale service.
Wholesale 18CrNiMo7-6 DIN 1.6587 Steel Round Rod Product Description DIN1.6587/18CrNiMo7-6 is a low carbon,case hardening (carburizing) steel which contains 1.8% chromium – nickel – molybdenum as strengthening agents as per EN 10084. Characterised by high core strength and toughness in medium to large sections with case hardness up to Rc62 when carburized, hardened and tempered,and it is also used in area of heavy and high strained gear parts with high demands on toughness at core tensile of 1050–1350N/mm2.DIN1.6587/18CrNiMo7-6 is same as 17CrNiMo6 steel,generally supplied in the annealed condition with a maximum brinell hardness of 229 Chemical Composition
| Standard | Grade | C | Mn | P | S | Si | Ni | Cr | Mo |
| EN 10084 | 18CrNiMo7-6 | 0.15-0.21 | 0.50-0.90 | ≤ 0.025 | ≤ 0.035 | ≤ 0.04 | 1.4-1.7 | 1.5-1.8 | 0.25-0.35 |
| 1.6587 |
Physical Property
| Density, g/cm3 | 7.85 | ||||
| Specific heat capacity J/(kg.K) | 460 | ||||
| Electric resistivity Ohm.mm2 /m | 0.18 | ||||
| Electric conductivity Siemens.m/mm2 | 5.55 | ||||
| Modulus of elasticity Gpa | 210 | ||||
| Thermal expansion 10^6 m/(m.K) | 100 ℃ | 200 ℃ | 300 ℃ | 400 ℃ | 500 ℃ |
| 11.1 | 12.1 | 12.9 | 13.5 | 13.9 | |
Mechanical Property
| Size mm | ≤ 11 | 12-30 | 31-63 |
| R Mpa | 1180-1420 | 1080-1320 | 980-1270 |
| Rp 0.2 Mpa | ≥ 835 | ≥785 | ≥ 685 |
| A % | ≥ 7 | ≥ 8 | ≥ 5 |
| C % | ≥ 30 | ≥ 35 | ≥ 35 |
| Kv J | ≥ 44 | ≥ 44 | |
| Hardness HB | 354-406 | 327-384 | 295-373 |
Forging DIN 1.6587 | 17CrNiMo6 |18CrNiMo7-6 forging temperature:900 – 1100°C,cool slowly in the sand after forged. Heat Treatment
-
Normalizing:850 – 880°C/air
-
Soft annealing:650 – 700°C/furnace
-
Stress relieve:630- 650oC
-
Carburising:880 – 980°C
-
Core hardening:830 – 870°C/water
-
Intermediate annealing:630 – 650°C
-
Case hardening:780 – 820°C/water
-
Tempering:150 – 200°C
Surface Hardness
-
Treated to improveshearability(+S):Max 255HB
-
Soft annealed(+A):Max 229HB
-
Treated to hardness range(+TH):179-229HB
-
Treated to ferrite-pearlite structure and hardness range(+FP):159-207HB
Application DIN 1.6587 | 17CrNiMo6 |18CrNiMo7-6 steel for the parts which require core tensile strength and high hardness. Susceptible to the large seized parts with high wearing resistance and loading such as: Heavy Duty Bushings and Bearings, Cam Followers, Clutch Dogs, Compressor Bolts, Extractors, Fan Shafts, Heavy Duty Gears, Pump Shafts, Sprockets, Tappets, Wear Pins, Wire Guides etc..
Related Products img src="/Content/upload/2020586095/202012301426407415489.webp.jpg" width="750" height="1236" alt="Wholesale 18CrNiMo7-6 DIN 1.6587 Steel Round Rod"> 
About packing
Hot Tags: wholesale 18crnimo7-6 din 1.6587 forged steel round rod, China, manufacturers, suppliers, factory, en36 hardness in hrc, Forged GB 20crmnti Alloy Steel Round Bar, JIS Snc815 12crni3 Alloy Steel Round Bar, Astm H12 Steel Bar Skd62 Steel Rod, Kovar Alloy 4J29 Bar, 35ncd16 Equivalent Material 1 6773