Sichuan Liaofu Special Steel Company is one of the most experienced manufacturers and suppliers of incoloy 901 round bar alloy 901 round bar in China. With over 20 years' experience, our factory offer high quality products made in China with competitive price. Welcome to contact us for wholesale service.
Technical specification can accroding to GB/ASTM ect STandards
Incoloy 901 Chemical composition:
| Alloy |
% |
Ni |
Cu |
Al |
Fe |
Ti |
Co |
Mn |
S |
C |
Si |
P |
Cr |
Mo |
B |
|
Incoloy 901 |
Min. |
40.0 |
2.35 |
11.0 |
5.0 |
0.01 |
|||||||||
|
Max. |
45.0 |
0.50 |
0.35 |
Balance |
3.10 |
1.0 |
1.0 |
0.03 |
0.10 |
0.60 |
0.03 |
14.0 |
7.0 |
0.02 |
Incoloy 901 Physical properties:
| Density |
8.14 g/cm3 |
|
Melting point |
1280-1345°C |
Incoloy 901 minimum mechanical properties( in the room temperature):
| Status |
Tensile strength |
Yield strength |
Elongation |
|
Incoloy 901 |
1034 |
689 |
12 |
Inconel 901 Description
A nickel-iron-chromium alloy containing titanium and aluminum for precipitation hardening and molybdenum for solid-solution strengthening. The alloy has high yield strength and creep resistance at temperatures to about 1110°F (600°C). A subtantial iron content enables the alloy to combine high strength with good forging characteristics. Used in gas turbines for discs and shafts. Standard products form is round.
Corrosion Resistance
Alloy 901 has good corrosion resistance to the atmospheres normally found in jet engine operations. It has slightly lower scaling resistance than such alloy as Types 309 and 310 stainless steel.
Hot Working
Alloy 901 is forged between 2050°F (1121°C) and 1850°F (1010°C), metal temperature. Light hot work may be continued down to 1600°F (871°C) but not below. Metal temperature should not exceed 2050°F (1121°C) during rapid working. Billets should be charged into a hot furnace and heated rapidly through the precipitation hardening range.
Alloy 901 can be welded by the inert-gas-arc method. It is difficult to weld. All welding should be done in the solution treated condition. Cold worked parts should be re-solution treated before welding. A re-solution treatment is recommended after welding before stabilizing and aging.
Hot Tags: incoloy 901 round bar alloy 901 round bar, China, manufacturers, suppliers, factory, 310S Stainless Steel Round Bar, 2205 Bright Stainless Steel, 253MA Stainless Steel Bar, 904L Hexagonal Stainless Steel, SS 410 Stainless Steel Solid Bar, ASTM A276 Cold Drawn 316L Stainless Steel Bar