We have developed high-quality, efficient Bearing Steel Bar, Alloy Steel Bar, 253MA Stainless Steel Bar technologies that have improved quality and productivity and placed us far ahead of the competition in the industry. We provide customers with high-quality and most valuable products and services, and win their understanding, respect and support with our sincerity and strength. The development of high technology and the realization of industrialization have become our steps towards modernity. We have extensive goods supply and the price is our advantage. We provide customers with one-stop services such as design, research and development, manufacturing, sales and installation.
Maraging 300 / VASCOMAX® 300 Steel - AMS 6514
Maraging 300 / VASCOMAX® 300 is an 18% nickel, cobalt strengthened steel (C-type) with excellent properties, workability and heat treatment characteristics. Maraging is double vacuum melted by VIM (Vacuum Induction Melt) followed by VAR (Vacuum Arc Remelt). Maraging material is supplied in the annealed and descaled condition. The alloy is very tough, relatively soft (RC 30/35), readily machined or formed. Maraging provides a high value for critical parts in aerospace, structural, component and tooling applications.
Service Steel Aerospace has Maraging / VASCOMAX® 300 available in billet, bar, rod, plate, sheet, and customized forgings
Maraging ;>MARtensitic - a very hard form of steel crystalline structure.Subsequent AGING (precipitation hardening - approx 3-6 hours @ 900ºF yields optimum material characteristics)
ADVANTAGES OF Maraging 300 Steel:
Excellent Mechanical Properties
|
Excellent Workability
|
Advantages During Application
|
Common Specifications:
|
Chemical Composition:
| Symbol | Element | Nominal % |
|---|---|---|
| C | Carbon | 0.03 max |
| Si | Silicon | 0.10 max |
| Mn | Manganese | 0.10 max |
| Ni | Nickel | 18.50 |
| Co | Cobalt | 9.00 |
| Mo | Molybdenum | 4.80 |
| Ti | Titanium | 0.60 |
| Al | Aluminum | 0.10 |
| Fe | Iron | Balance |
Physical Properties:
| Property | |
|---|---|
| Density, lb /in3 | .289 |
| Modulus of Elasticity | 27.5 x 10-6 psi |
| Average Co of Thermal Expansion | 5.6 x 10-6 in/in/°F |
Heat Treatment / Aging:
Maraging alloys are essentially carbon-free, a protective atmosphere is not required during annealing or aging. Material is supplied in the solution annealed condition with a hardness of 30/35 Rc. Typical heat treat time/temperature are listed below. Large cross sections should be aged for longer periods.
| Temperature | Time | Resulting Hardness |
|---|---|---|
| 900/925 °F | 6 hrs | 50/55 Rc |
NOTE: A modified aging cycle is suggested for die casting applications for increased die life. The following thermal treatments have been used to obtain desirable characteristics for die casters. Following the rough machining of the die, anneal at 1500-1525 ºF for 1 hour per inch of thickness is typical. After finish machining, an aging heat treatment of 980-1000 ºF for 6 hours is typical.
VASCOMAX® is a registered trademark of Allegheny Technologies Incorporated / Allvac.
We'll make every effort and hard work being outstanding and excellent, and speed up our techniques for Maraging C-350 (C-300, C-250, C-200) Forged/Forging Round Bars. Establish long term and win-win business relationships with all our customers, share the success and enjoy the happiness of spreading our products to the world together. Since the establishment of our company, we have been cooperating with colleagues from all walks of life with the most sincere heart, absorbing the essence and eliminating the dross in the cooperation, in order to maximize the development.