High-Speed Tool Steel HS6-5-2-5 M35 W6mo5cr4 V2co5 Pipe&Tube

Since the establishment, our company has always practiced the concept of science-led development, accumulated experience in the Gr2 Titanium Wire, 440C Stainless Steel Plate, ASTM B348 Grade 5 titanium rectangle rod field, so as to provide users with high-quality and reliable products. Our company pays attention to enterprise innovation and development in re-innovation and has achieved good economic and social benefits. We wish to work with you and seek common development. Our company adheres to the business philosophy of 'professional diligence, honesty, altruism, and win-win'. From the actual needs of the market, we strive to create a trustworthy corporate image. In line with the principle of customer-oriented, we strictly manage, constantly improve the technical level and pursue excellence.

M35 High speed steel plate

M35 cobalt high-speed steel, when compared to lower-priced alternatives that are easier to process, can achieve exceptional hardness (HRC 67-70) and elevated red hardness (HRC 63-65 at 625°C for 4 hours) through appropriate heat treatment. It also exhibits superior wear resistance while maintaining toughness and bending strength comparable to standard high-speed steels, effectively mitigating issues such as edge collapse and cracking in molds.

The primary characteristic of M35 high-speed steel is its cobalt content, which enhances its performance as a universal cutting tool die steel with quenching hardness ranging from 1200°C to 1240°C. Its main applications include hobs, broaches, and end milling cutters.

Standard comparisons include: AISI-M2 and JIS-SKH51.

Factory conditions involve spheroidizing annealing below 225°C.

Features and Applications: This tungsten-based high-speed steel is ideal for manufacturing tools that require both wear resistance and impact resilience for robust cutting operations. It is suitable for advanced punching dies, screw dies, tools necessitating toughness in complex shapes, reamers, milling cutters, iron heads, punches etc.

Forging temperature ranges from 1100°C to 900°C.

Annealing involves heating the material to between 800°C and 850°C; it should be held at this temperature for approximately 2-4 hours before cooling within the furnace.

Cooling mediums may include air cooling or oil quenching followed by grading at temperatures between 550°C and 580°C.

Product Basic Information:

Designation by Standards

Chemical Composition (in weight %)

Physical properties (avarage values) at ambient temperature of M35 High speed steel plate

Modulus of elasticity [103 x N/mm2]: 217
Density [g/cm3]: 8.1
Thermal conductivity [W/m.K]: 19.0
Electric resistivity [Ohm mm2/m]: 0.60
Specific heat capacity[J/g.K]: 0.46

Coefficient of Linear Thermal Expansion 10-6 oC-1

Soft Annealing
Heat to 820-880oC, cool slowly in furnace. This will produce a maximum Brinell hardness of 230-300.

Stress Relieving
Stress relieving to remove machining stresses should be carried out by heating to 650oC, holding for one hour at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.

Hardening
Heat to 450-600oC, preheat to 850oC and then to 1050oC. Harden from a temperature of 1210-1250oC followed by oil, air quenching or warm bath 550oC. Hardness after quenching is 64-66 HRC.

Transformation temperatures: Ac1=824oC , Ac3=853oC.

Tempering
Tempering temperature: 3 x 1 hour at 540-570oC.

M35 High speed steel plate Tempering Temperature (oC) vs. Hardness (HRC)

Typical application examples:

① Suitable for producing various types of high-performance saw blades drills taps broaches hobs along with an array of milling cutters.

② Cold forging dies deep drawing dies cutting tools etc.

③ Recommended for industries involved in watch case production screw manufacturing among other cold stamping applications.

Our Service

That has a positive and progressive attitude to customer's interest, our organization consistently improves our products quality to satisfy the demands of shoppers and further focuses on safety, reliability, environmental specifications, and innovation of High-Speed Tool Steel HS6-5-2-5 M35 W6mo5cr4 V2co5 Pipe&Tube. With the business philosophy of 'quality service promotes product sales', we forge ahead in the industry. The high-quality service solves the worries for many users and wins the high praise and trust of them! Our workers can improve the product to customer's demand at any time, and can provide reliable technical support for long-term development.