We adhere to the tenet of 'Science and technology as the guide, quality for survival, management for development', and strive to provide customers with high-quality 4140 Steel Shaft, Alloy Steel Bar, 180 Degree Titanium Elbow Bend pipe solutions. Our sales network has successfully spread all over the world, our products are deeply trusted and praised by customers, and the related supporting industry chain is perfect. With years of experience in design and manufacturing, driven by technological innovation, we provide customers with comprehensive, integrated and high value-added services and products to meet the continuous development needs of new and old friends at home and abroad.
Introduction
630 stainless steel rod is widely used in high strength parts that require both rust resistance and weak acid, alkali and salt corrosion, such as turbine blades at the end stage, and structural parts that work at a temperature below 300℃ in corrosive environment.
Heat treatment process of SUS630
Heat treatment specification
Solution 1020~1060℃ fast cooling;
2) Aging at 480℃, after solution treatment, air cooling at 470~490℃;
3) Aging at 550℃, after solution treatment, air cooling at 540~560℃;
4) Aging at 580℃, after solution treatment, air cooling at 570~590℃;
5) Aging at 620℃, after solution treatment, air cooling at 610~630℃. Metallographic structure: The microstructure is characterized by precipitation hardening type.
SUS630 is martensitic precipitated hardened stainless steel, with high strength, high hardness, good welding performance and corrosion resistance. It has been widely used in valve, shaft and chemical fiber industry and high strength parts with certain corrosion resistance requirements. SUS630 is martensitic precipitated stainless steel SUS630 special addition of copper precipitated hardening type steel.
SUS630 Stainless Steel (Japan brand)0Cr17Ni4Cu4Nb(China brand) Stainless steel: SUS630 features precipitation hardened steel with added copper. Used for manufacturing shaft and steam turbine components. Precipitation-hardened martensitic stainless steel composed of copper and niobium/columbium has low carbon content, better corrosion resistance and weldability than ordinary martensitic stainless steel, similar to 18-8 stainless steel, with simple heat treatment process and good machinability, but it is difficult to meet the cryogenic processing. Metallographic structure: The microstructure is characterized by precipitation hardening type. Use for manufacturing high corrosion resistance, high strength parts, such as bearings, steam turbine parts. Physical property
Material | ASTM 630 | ||
Chemical Composition | Mechanical Properties(In Quenched & Tempered State) 480 °C | ||
C | <0.07 | Tensile strength(MPA) | >1180 |
Si | <1.00 | Yield strength (MPA) | >1130 |
Mn | <1.00 | Elongation(δ5/%) | >10 |
Cr | 15.50-17.50 | Reduction in Area (ψ/%) | >40 |
Mo | - | Impact (J)v | - |
P | ≤0.035 | Hardness | <375 |
S | ≤0..030 | ||
N | - | ||
Ni | 3.00-5.00 | ||
What advantages do you have with your peers?
1. We are factory direct sales, affordable, and product quality is guaranteed.
2. We have a professional technical R & D team and obtained a number of product patent certifications in the industry.
3. We are a Chinese government-supported enterprise and a key support enterprise, strictly controlling product quality production.
4. We have a complete production line to ensure that your products are completed on time and with quality.
Our Service
Our AISI 630 Stainless Steel Round Bar (17-7pH 17-4pH 15-5pH), which are designed and made based on our customers' requirements, are praised through our untiring efforts and hard work. Brand must be another name for improving the quality, the concentration of customer satisfaction and the result of the recognition of the majority of users. It using the world's leading system for reliable operation, a low failure rate, it is suitable for customers choice.