After years of hard work, the quality of the Aisi 304 Seamless Steel Pipe, Spring Steel, Titanium elbow bend fitting pipe has been greatly improved, and has received unanimous praise from the same industry. You can rest assured to buy from us. Our products are sold to the many countries, and are favorably appraised by clients. Our company is committed to bringing an innovative and efficient product procurement experience to companies pursuing high efficiency and low cost so that they can reduce comprehensive procurement costs. We sincerely welcome friends from all walks of life to visit, investigate and negotiate business! We are committed to building meaningful, inclusive and empowering corporate values, and strive to letting this open, global, and innovative ecosystem release unlimited possibilities.
Introduction
630 stainless steel rod is widely used in high strength parts that require both rust resistance and weak acid, alkali and salt corrosion, such as turbine blades at the end stage, and structural parts that work at a temperature below 300℃ in corrosive environment.
Heat treatment process of SUS630
Heat treatment specification
Solution 1020~1060℃ fast cooling;
2) Aging at 480℃, after solution treatment, air cooling at 470~490℃;
3) Aging at 550℃, after solution treatment, air cooling at 540~560℃;
4) Aging at 580℃, after solution treatment, air cooling at 570~590℃;
5) Aging at 620℃, after solution treatment, air cooling at 610~630℃. Metallographic structure: The microstructure is characterized by precipitation hardening type.
SUS630 is martensitic precipitated hardened stainless steel, with high strength, high hardness, good welding performance and corrosion resistance. It has been widely used in valve, shaft and chemical fiber industry and high strength parts with certain corrosion resistance requirements. SUS630 is martensitic precipitated stainless steel SUS630 special addition of copper precipitated hardening type steel.
SUS630 Stainless Steel (Japan brand)0Cr17Ni4Cu4Nb(China brand) Stainless steel: SUS630 features precipitation hardened steel with added copper. Used for manufacturing shaft and steam turbine components. Precipitation-hardened martensitic stainless steel composed of copper and niobium/columbium has low carbon content, better corrosion resistance and weldability than ordinary martensitic stainless steel, similar to 18-8 stainless steel, with simple heat treatment process and good machinability, but it is difficult to meet the cryogenic processing. Metallographic structure: The microstructure is characterized by precipitation hardening type. Use for manufacturing high corrosion resistance, high strength parts, such as bearings, steam turbine parts. Physical property
Material | ASTM 630 | ||
Chemical Composition | Mechanical Properties(In Quenched & Tempered State) 480 °C | ||
C | <0.07 | Tensile strength(MPA) | >1180 |
Si | <1.00 | Yield strength (MPA) | >1130 |
Mn | <1.00 | Elongation(δ5/%) | >10 |
Cr | 15.50-17.50 | Reduction in Area (ψ/%) | >40 |
Mo | - | Impact (J)v | - |
P | ≤0.035 | Hardness | <375 |
S | ≤0..030 | ||
N | - | ||
Ni | 3.00-5.00 | ||
What advantages do you have with your peers?
1. We are factory direct sales, affordable, and product quality is guaranteed.
2. We have a professional technical R & D team and obtained a number of product patent certifications in the industry.
3. We are a Chinese government-supported enterprise and a key support enterprise, strictly controlling product quality production.
4. We have a complete production line to ensure that your products are completed on time and with quality.
Our Service
We take pleasure in an extremely fantastic standing among the our prospects for 630 Stainless Steel Bright Round Bar. We not only lead the industry in terms of brand, supply, and service, but also can provide customers with timely and feasible technical support and overall services to satisfy different customers at multiple levels demand. The main intention of our firm is to build up a satisfying memory for all consumers, and set up a long-term win-win small business connection.