1.2379 D2 steel is a high carbon – high chromium air hardening tool steel, heat treatable to 60-62 HRC . D2 offers excellent wear and abrasion resistance, due to large volumes of carbides in the micro-structure. X153CrMoV12/1.2379 D2 tool steel is a high carbon, high chromium tool steel...

Sichuan Liaofu Special Steel Company is one of the most experienced manufacturers and suppliers of x153crmov12 high carbon tool steel in China. With over 20 years' experience, our factory offer high quality products made in China with competitive price. Welcome to contact us for wholesale service.

The chemical composition of X153CrMoV12 includes elements such as carbon, chromium, molybdenum and vanadium. These elements work together to give this steel its unique properties. For example, carbon gives it hardness and wear resistance, while chromium gives it high corrosion resistance. Molybdenum and vanadium enhance its toughness, making it resistant to cracking and breakage.

X153CrMoV12 also has easy processing and excellent polishing ability, this steel is relatively easy to work and can be polished to a mirror-like finish. This makes it ideal for use in precision and surface quality precision applications, often in the manufacture of tools, molds and springs.

Material

Material		AISI D2
Chemical Composition		Mechanical Properties(In Quenched & Tempered State)
C	1.40-1.60	Tensile strength(MPA)	-
Si	<0.60	Yield strength (MPA)	-
Mn	<0.60	Elongation(δ5/%)	--
Cr	11.00-13.00	Reduction in Area (ψ/%)	-
Mo	0.70-1.20	Impact (J)	-
P	≤0.030	Brinell Hardness (HBW)	<255 cooling with OIL temperature 790+_15c
S	≤0..030
Cu	-
Ni	-

Mechanical and physical properties of AISI D2, 1.2379, X153CrMoV12

Hardness of steel after softening annealing: ≤ 255 HB.

Hardness after hardening: ≥ 60 HRC.

Hardness after hardening and tempering at temperature:

200C = ≥ 60 HRC

250C = 58.2 HRC

300C = 58 HRC

350C = 58 HRC

400C = 58.5 HRC

450C = 58.8 HRC

500C = 55.2 HRC

550C = 50 HRC

FAQ:

What material is X153CrMoV12?

The material 1.2379 is a ledeburitic cold work tool steel with high wear resistance and good cutting strength. A high resistance to abrasive and adhesive wear and high pressure resistance are given. Due to the good mechanical properties, this steel can be used in many different applications.

Is Cr12MoV better than D2?

Cr12MoV tends to have better toughness compared to AISI D2. This allows it to absorb more impact without fracturing, making it suitable for certain applications where impact resistance is essential. AISI D2, on the other hand, offers higher strength due to its higher carbon and molybdenum content.